Sutton Tools | Techline
View ProductDrills, Carbide, Centre
Designed to maintain accurate centre holes on long production runs
Also used to ensure accurate starting and centring when precision drilling is required
Suitable for materials up to 1600N/mm2
ISO | VDI | Description | Condition | Hardness | Strength | Optimal |
---|---|---|---|---|---|---|
P | 1 | Steel - Non-alloy, cast & free cutting (~ 0.15 %C) | Annealed | 125HB | 440MPa | |
P | 2 | Steel - Non-alloy, cast & free cutting (~ 0.45 %C) | Annealed | 190HB | 640MPa | |
P | 3 | Steel - Non-alloy, cast & free cutting (~ 0.45 %C) | Quenched & Tempered | 250MPa | 840MPa | |
P | 4 | Steel - Non-alloy, cast & free cutting (~ 0.75 %C) | Annealed | 270MPa | 910MPa | |
P | 5 | Steel - Non-alloy, cast & free cutting (~ 0.75 %C) | Quenched & Tempered | 300MPa | 1010MPa | |
P | 6 | Steel - Low alloy & cast < 5% of alloying elements | Annealed | 180HB | 610MPa | |
P | 7 | Steel - Low alloy & cast < 5% of alloying elements | Quenched & Tempered | 275MPa | 930MPa | |
P | 8 | Steel - Low alloy & cast < 5% of alloying elements | Quenched & Tempered | 300MPa | 1010MPa | |
P | 9 | Steel - Low alloy & cast < 5% of alloying elements | Quenched & Tempered | 350HB | 1180MPa | |
P | 10 | Steel - High alloy, cast & tool | Annealed | 200MPa | 680MPa | |
P | 11 | Steel - High alloy, cast & tool | Hardened & Tempered | 325HB | 1100MPa | |
P | 12 | Steel - Corrosion resistant & cast - Ferritic / Martensitic | Annealed | 200HB | 680MPa | |
P | 13 | Steel - Corrosion resistant & cast - Martensitic | Quenched & Tempered | 240HB | 810MPa | |
M | 14.1 | Stainless Steel - Austenitic | Age Hardened | 180MPa | 610MPa | |
M | 14.2 | Stainless Steel - Duplex | 250MPa | 840MPa | ||
M | 14.3 | Stainless Steel - Precipitation Hardening | 250MPa | 840MPa | ||
K | 15 | Cast Iron, Grey (GG) - Ferritic / Pearlitic | 180MPa | 610MPa | ||
K | 16 | Cast Iron, Grey (GG) - Pearlitic | 260MPa | 880MPa | ||
K | 17 | Cast Iron, Nodular (GGG) - Ferritic | 160MPa | 570MPa | ||
K | 18 | Cast Iron, Nodular (GGG) - Pearlitic | 250MPa | 840MPa | ||
K | 19 | Cast Iron, Malleable - Ferritic | 130MPa | 460MPa | ||
K | 20 | Cast Iron, Malleable - Pearlitic | 230MPa | 780MPa | ||
N | 21 | Aluminum & Magnesium, wrought alloy - Non Heat Treatable | 60MPa | 210MPa | ||
N | 22 | Aluminum & Magnesium, wrought alloy - Heat Treatable | Age Hardened | 100MPa | 360MPa | |
N | 23 | Aluminum & Magnesium, cast alloy ?12% Si - Non Heat Treatable | 75MPa | 270MPa | ||
N | 24 | Aluminum & Magnesium, cast alloy ?12% Si - Heat Treatable | Age Hardened | 90MPa | 320MPa | |
N | 25 | Aluminum & Magnesium, cast alloy >12% Si - Non Heat Treatable | 130MPa | 460MPa | ||
N | 26 | Copper & Copper alloys (Brass/Bronze) - Free cutting, Pb > 1% | 110MPa | 390MPa | ||
N | 27 | Copper & Copper alloys (Brass/Bronze) - Brass (CuZn, CuSnZn) | 90MPa | 320MPa | ||
N | 28 | Copper & Copper alloys (Brass/Bronze) - Bronze (CuSn) | 100MPa | 360MPa | ||
N | 29 | Non-metallic - Thermosetting & fiber-reinforced plastics | ||||
N | 30 | Non-metallic - Hard rubber, wood etc. | ||||
S | 31 | High temperature alloys - Fe based | Annealed | 200HB | 680MPa | |
S | 32 | High temperature alloys - Fe based | Age Hardened | 280HB | 950MPa | |
S | 33 | High temperature alloys - Ni / Co based | Annealed | 250HB | 840MPa | |
S | 34 | High temperature alloys - Ni / Co based | Age Hardened | 350HB | 1180MPa | |
S | 35 | High temperature alloys - Ni / Co based | Cast | 320HB | 1080MPa | |
S | 36 | Titanium & Titanium alloys - CP Titanium | 400MPa | |||
S | 37.1 | Titanium & Titanium alloys - Alpha alloys | 860MPa | |||
S | 37.2 | Titanium & Titanium alloys - Alpha / Beta alloys | Annealed | 960MPa | ||
S | 37.3 | Titanium & Titanium alloys - Alpha / Beta alloys | Age Hardened | 1170MPa | ||
S | 37.4 | Titanium & Titanium alloys - Beta alloys | Annealed | 830MPa | ||
S | 37.5 | Titanium & Titanium alloys - Beta alloys | Age Hardened | 1400MPa | ||
H | 38.1 | Hardened steel | Hardened & Tempered | 45 | ||
H | 38.2 | Hardened steel | Hardened & Tempered | 55 | ||
H | 39.1 | Hardened steel | Hardened & Tempered | 58 | ||
H | 39.2 | Hardened steel | Hardened & Tempered | 62 | ||
H | 40 | Cast Iron - Chilled | Cast | 400MPa | 1350MPa | |
H | 41 | Cast Iron | Hardened & Tempered | 55 |