Sutton Tools, Techline
View ProductSutton Tools TiNite® jobber drills are for high performance drilling. Lasts up to 6 times longer than standard HSS drill bits. For drilling metal & tougher alloy steels such as steel, stainless steel, copper, brass, aluminium & cast iron.
Cuts faster at higher speeds
118° web thinned point reduces the amount of thrust required
Precision ground flute offers high accuracy drilling and fast chip removal
Made from M2 High Speed Steel (HSS) offering the best combination of strength, heat & wear resistance
TiN coating provides 3 to 6 times longer tool life than uncoated tools and is suitable for general purpose use in a wide range of applications
ISO | VDI | Description | Condition | Hardness | Strength | Optimal |
---|---|---|---|---|---|---|
P | 1 | Steel - Non-alloy, cast & free cutting (~ 0.15 %C) | Annealed | 125MPa | 440MPa | |
P | 2 | Steel - Non-alloy, cast & free cutting (~ 0.45 %C) | Annealed | 190MPa | 640MPa | |
P | 3 | Steel - Non-alloy, cast & free cutting (~ 0.45 %C) | Quenched & Tempered | 250MPa | 840MPa | |
P | 4 | Steel - Non-alloy, cast & free cutting (~ 0.75 %C) | Annealed | 270MPa | 910MPa | |
P | 5 | Steel - Non-alloy, cast & free cutting (~ 0.75 %C) | Quenched & Tempered | 300MPa | 1010MPa | |
P | 6 | Steel - Low alloy & cast < 5% of alloying elements | Annealed | 180MPa | 610MPa | |
P | 7 | Steel - Low alloy & cast < 5% of alloying elements | Quenched & Tempered | 275MPa | 930MPa | |
P | 8 | Steel - Low alloy & cast < 5% of alloying elements | Quenched & Tempered | 300MPa | 1010MPa | |
P | 9 | Steel - Low alloy & cast < 5% of alloying elements | Quenched & Tempered | 350MPa | 1180MPa | |
P | 10 | Steel - High alloy, cast & tool | Annealed | 200MPa | 680MPa | |
P | 11 | Steel - High alloy, cast & tool | Hardened & Tempered | 325MPa | 1100MPa | |
P | 12 | Steel - Corrosion resistant & cast - Ferritic / Martensitic | Annealed | 200MPa | 680MPa | |
P | 13 | Steel - Corrosion resistant & cast - Martensitic | Quenched & Tempered | 240MPa | 810MPa | |
M | 14.1 | Stainless Steel - Austenitic | Age Hardened | 180MPa | 610MPa | |
M | 14.2 | Stainless Steel - Duplex | 250MPa | 840MPa | ||
M | 14.3 | Stainless Steel - Precipitation Hardening | 250HB | 840MPa | ||
K | 15 | Cast Iron, Grey (GG) - Ferritic / Pearlitic | 180HB | 610MPa | ||
K | 16 | Cast Iron, Grey (GG) - Pearlitic | 260HB | 880MPa | ||
K | 17 | Cast Iron, Nodular (GGG) - Ferritic | 160HB | 570MPa | ||
K | 18 | Cast Iron, Nodular (GGG) - Pearlitic | 250HB | 840MPa | ||
K | 19 | Cast Iron, Malleable - Ferritic | 130HB | 460MPa | ||
K | 20 | Cast Iron, Malleable - Pearlitic | 230HB | 780MPa | ||
N | 21 | Aluminum & Magnesium, wrought alloy - Non Heat Treatable | 60HB | 210MPa | ||
N | 22 | Aluminum & Magnesium, wrought alloy - Heat Treatable | Age Hardened | 100HB | 360MPa | |
N | 23 | Aluminum & Magnesium, cast alloy ≤12% Si - Non Heat Treatabl | 75HB | 270MPa | ||
N | 24 | Aluminum & Magnesium, cast alloy ≤12% Si - Heat Treatable | Age Hardened | 90HB | 320MPa | |
N | 25 | Aluminum & Magnesium, cast alloy >12% Si - Non Heat Treatabl | 130HB | 460MPa | ||
N | 26 | Copper & Copper alloys (Brass/Bronze) - Free cutting, Pb > 1 | 110HB | 390MPa | ||
N | 27 | Copper & Copper alloys (Brass/Bronze) - Brass (CuZn, CuSnZn) | 90HB | 320MPa | ||
N | 28 | Copper & Copper alloys (Brass/Bronze) - Bronze (CuSn) | 100HB | 360MPa | ||
N | 29 | Non-metallic - Thermosetting & fiber-reinforced plastics | ||||
N | 30 | Non-metallic - Hard rubber, wood etc. | ||||
S | 31 | High temperature alloys - Fe based | Annealed | 200HB | 680MPa | |
S | 32 | High temperature alloys - Fe based | Age Hardened | 280HB | 950MPa | |
S | 33 | High temperature alloys - Ni / Co based | Annealed | 250HB | 840MPa | |
S | 34 | High temperature alloys - Ni / Co based | Age Hardened | 350HB | 1180MPa | |
S | 35 | High temperature alloys - Ni / Co based | Cast | 320HB | 1080MPa | |
S | 36 | Titanium & Titanium alloys - CP Titanium | 400MPa | |||
S | 37.1 | Titanium & Titanium alloys - Alpha alloys | 860MPa | |||
S | 37.2 | Titanium & Titanium alloys - Alpha / Beta alloys | Annealed | 960MPa | ||
S | 37.3 | Titanium & Titanium alloys - Alpha / Beta alloys | Age Hardened | 1170MPa | ||
S | 37.4 | Titanium & Titanium alloys - Beta alloys | Annealed | 830MPa | ||
S | 37.5 | Titanium & Titanium alloys - Beta alloys | Age Hardened | 1400MPa | ||
H | 38.1 | Hardened steel | Hardened & Tempered | 45HRC | ||
H | 38.2 | Hardened steel | Hardened & Tempered | 55HRC | ||
H | 39.1 | Hardened steel | Hardened & Tempered | 58HRC | ||
H | 39.2 | Hardened steel | Hardened & Tempered | 62HRC | ||
H | 40 | Cast Iron - Chilled | Cast | 400HB | 1350MPa | |
H | 41 | Cast Iron | Hardened & Tempered | 55HRC |